Deng, Jinxia and Li, Lihong and Chen, Jun and Yu, Ranbo and Xing, Xianran (2012) Facile molten salt synthesis of ordered perovskite Ba(Sr 1/3Nb 2/3)O3 powders. Inorganic Chemistry Communications, 21. pp. 92-95. ISSN 1387-7003
Abstract
Extra large Alkaline-earth Sr 2 + cation was successfully introduced into the B′-site of the complex perovskite A(B′ 1/3B″ 2/3)O 3 by a molten salt synthesis method. The crystal structure of the as-synthesized Ba(Sr 1/3Nb 2/3)O 3 was determined by Rietveld refinement of X-ray diffraction and Raman spectrum. The results showed that the as-synthesized Ba(Sr 1/3Nb 2/3)O 3 had the 1:2 order-disorder trigonal perovskite structure, which was also an isometric compound of hexagonal BaTiO 3-type structure Ba 3SrNb 2O 9. The measured dielectric properties on the perovskite Ba(Sr 1/3Nb 2/3)O 3 ceramics showed the good frequency stability and the low dielectric loss.
![]() |
Statistics for this ePrint Item |
Item Type: | Article (Commonwealth Reporting Category C) |
---|---|
Refereed: | Yes |
Item Status: | Live Archive |
Additional Information: | Files associated with this item cannot be displayed due to copyright restrictions. |
Faculty/School / Institute/Centre: | No Faculty |
Faculty/School / Institute/Centre: | No Faculty |
Date Deposited: | 14 Jun 2017 01:36 |
Last Modified: | 14 Jun 2017 01:36 |
Uncontrolled Keywords: | Ba(Sr 1/3Nb 2/3)O3; Complex perovskite; Molten salt synthesis; Raman; X-ray diffraction; |
Fields of Research (2008): | 03 Chemical Sciences > 0302 Inorganic Chemistry > 030299 Inorganic Chemistry not elsewhere classified |
Socio-Economic Objectives (2008): | E Expanding Knowledge > 97 Expanding Knowledge > 970103 Expanding Knowledge in the Chemical Sciences |
Identification Number or DOI: | https://doi.org/10.1016/j.inoche.2012.04.021 |
URI: | http://eprints.usq.edu.au/id/eprint/31980 |
Actions (login required)
![]() |
Archive Repository Staff Only |