Investigation on the fatigue behaviour of pultruded fibre composites

Taylor, Alan Owen (2009) Investigation on the fatigue behaviour of pultruded fibre composites. [USQ Project] (Unpublished)

[img] PDF (Accepted Version)
Taylor_A_2009.pdf

Download (4Mb)

Abstract

Fibre composites existence in civil infrastructure and transportation is relatively new. Originally developed for aerospace, defence force and marine industries, composite materials did not make an appearance into large civil structures until the first legal road bridge was constructed in 2002. They have many advantages over conventional materials such as improved durability and high strength to weight ratio just to name a few. The behaviour of pultruded fibre composites has been studied to help the design engineer to better understand the long term performance of composite structures. This research project seeks to investigate the fatigue behaviour of pultruded fibre composites to help develop the fatigue curve or better known as the fatigue life of a material. Firstly a literature review was undertaken to help better understand the theory behind fibre composites and secondly a series of small scale (coupons) and large scale (Composite bridge girder) testing was done to prove these theories. This project also aimed to determine whether small scale testing can predict the fatigue life of large scale composite structures. Fatigue testing is a lengthy process with many researchers spending years just to develop one fatigue curve. Testing a particular sample to one million cycles at one hertz for example takes roughly 12 days to complete, and this does not including setup time. It may seem like the results obtained throughout this research project are quite small, however that one fatigue curve that is obtained is extremely important for the long term performance of pultruded fibre composites. By applying a prediction model to the small scale experimental data, the fatigue curve was developed. Initial results were not quite what were expected, however they did provide an insight into the fatigue performance of coupon testing as this was something that had never been done before on these products. There are minor flaws in the coupon testing, however these did not become apparent until final tests were completed. Further research into the use of coupons for fatigue testing purposes would be recommended. The composite bridge girder on the other hand showed extremely satisfying results considering it was tested at more than double the serviceability load specified by the Queensland Department of Main Roads


Statistics for USQ ePrint 8523
Statistics for this ePrint Item
Item Type: USQ Project
Refereed: No
Item Status: Live Archive
Depositing User: epEditor USQ
Faculty / Department / School: Historic - Faculty of Engineering and Surveying - Department of Agricultural, Civil and Environmental Engineering
Date Deposited: 26 Jul 2010 04:22
Last Modified: 21 Sep 2012 03:37
Uncontrolled Keywords: fibre composites; materials testing; fatigue
Fields of Research (FOR2008): 09 Engineering > 0905 Civil Engineering > 090503 Construction Materials
09 Engineering > 0912 Materials Engineering > 091202 Composite and Hybrid Materials
09 Engineering > 0913 Mechanical Engineering > 091307 Numerical Modelling and Mechanical Characterisation
Socio-Economic Objective (SEO2008): E Expanding Knowledge > 97 Expanding Knowledge > 970109 Expanding Knowledge in Engineering
URI: http://eprints.usq.edu.au/id/eprint/8523

Actions (login required)

View Item Archive Repository Staff Only